Miniature handheld digital optical microscopy, microenergy dispersive Xray fluorescence (EDXRF) spectroscopy and Xray diffraction (XRD) were used to systematically analyze ceramic samples from the Guangdong folk art museum in order to understand their manufacturing technique. The analysis indicates that the ceramic bodies all have high SiO₂ and low Al₂O₃ contents. The bodies also have a high content of Fe₂O₃. The glaze belongs to hightemperature calcium type. Wood ashes are likely to have been used as a flux in the samples. ZnO was found in the glaze. In the middle and later periods of the Qing Dynasty, the firing temperature of the ceramics was higher than 1100℃, and in the Republic of China period the firing temperature was even higher than 1200℃. These analytical results provide useful information regarding the manufacture of decorative ridge ceramic figurines from Shiwan, Guangdong Province.